LAIS is 100% Unique Worldwide and Quarried, Processed, Traded Solely from Solakis Marble.
It is being excavated since 1984, is proven to be a material that can be used for Indoor Commercial or Residential Projects.
LAIS marble is a Hard & Dense Dolomite, composed also of app. 20% calcite as well.
| PHYSICAL MECHANICAL PROPERTIES | M.O / AV. |
|---|---|
| Apparent specific weight (DIN 52102) | 2.827 kg/m3 |
| Porosity & Water accessible porosity determination (DIN 52102) | 0,51 wt% |
| Absorption Coefficient (DIN 52103) | 0,18 wt% |
| Modulus Elasticity (ASTM C-170) | 33 GPa |
| Compressive Strenght-Dry Condition (DIN 52105) | 174,4 N/mm2 |
| Compressive Strenght-Wet Condition (DIN 52105) | 195,0 N/mm2 |
| Modulus of Rupture-Dry Condition (DIN 52112) | 15,83 Mpa |
| Modulus of Rupture-Wet Condition (DIN 52112) | 9,80 Mpa |
| Compressive Strenght after freezing and thaw cycles (DIN 52104 & 52105) | 192,1 N/mm2 |
| Abrasion Resistance (DIN 52108) | 2,14 mm |
| Impact Strength (UNI-U 32.07.248.0) | 40 cm |